C79600 Nickel Silver vs. EN 1.4362 Stainless Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.4362 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.4362 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 15
25
Poisson's Ratio 0.3
0.27
Shear Modulus, GPa 43
79
Shear Strength, MPa 290
470
Tensile Strength: Ultimate (UTS), MPa 480
730
Tensile Strength: Yield (Proof), MPa 300
460

Thermal Properties

Latent Heat of Fusion, J/g 180
290
Maximum Temperature: Mechanical, °C 130
1060
Melting Completion (Liquidus), °C 930
1420
Melting Onset (Solidus), °C 880
1380
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 36
15
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
14
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 3.5
2.9
Embodied Energy, MJ/kg 57
41
Embodied Water, L/kg 310
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
160
Resilience: Unit (Modulus of Resilience), kJ/m3 400
530
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
26
Strength to Weight: Bending, points 17
23
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 15
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
22 to 24.5
Copper (Cu), % 43.5 to 46.5
0.1 to 0.6
Iron (Fe), % 0
65.5 to 74.3
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 0
0.1 to 0.6
Nickel (Ni), % 9.0 to 11
3.5 to 5.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0