C79600 Nickel Silver vs. EN 1.4922 Stainless Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.4922 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.4922 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 15
16
Poisson's Ratio 0.3
0.28
Shear Modulus, GPa 43
76
Shear Strength, MPa 290
470
Tensile Strength: Ultimate (UTS), MPa 480
770
Tensile Strength: Yield (Proof), MPa 300
550

Thermal Properties

Latent Heat of Fusion, J/g 180
270
Maximum Temperature: Mechanical, °C 130
720
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 880
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 36
24
Thermal Expansion, µm/m-K 21
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
7.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
2.8
Embodied Energy, MJ/kg 57
40
Embodied Water, L/kg 310
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
110
Resilience: Unit (Modulus of Resilience), kJ/m3 400
770
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 12
6.5
Thermal Shock Resistance, points 15
27

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.17 to 0.23
Chromium (Cr), % 0
10 to 12.5
Copper (Cu), % 43.5 to 46.5
0
Iron (Fe), % 0
83.5 to 88.2
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0.3 to 1.0
Molybdenum (Mo), % 0
0.8 to 1.2
Nickel (Ni), % 9.0 to 11
0.3 to 0.8
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Vanadium (V), % 0
0.2 to 0.35
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0