MakeItFrom.com
Menu (ESC)

C79600 Nickel Silver vs. EN 1.7202 Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.7202 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.7202 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 43
73
Tensile Strength: Ultimate (UTS), MPa 480
530 to 1810

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 130
420
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 880
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 36
46
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.5
Embodied Energy, MJ/kg 57
20
Embodied Water, L/kg 310
51

Common Calculations

Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
19 to 64
Strength to Weight: Bending, points 17
19 to 42
Thermal Diffusivity, mm2/s 12
12
Thermal Shock Resistance, points 15
16 to 53

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.35 to 0.4
Chromium (Cr), % 0
0.9 to 1.2
Copper (Cu), % 43.5 to 46.5
0 to 0.25
Iron (Fe), % 0
96.6 to 98
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0.6 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0