C79600 Nickel Silver vs. EN 1.8503 Steel

C79600 nickel silver belongs to the copper alloys classification, while EN 1.8503 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is EN 1.8503 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 15
16
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 43
73
Shear Strength, MPa 290
610
Tensile Strength: Ultimate (UTS), MPa 480
1000
Tensile Strength: Yield (Proof), MPa 300
910

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 130
440
Melting Completion (Liquidus), °C 930
1470
Melting Onset (Solidus), °C 880
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 36
41
Thermal Expansion, µm/m-K 21
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.5
2.3
Embodied Energy, MJ/kg 57
33
Embodied Water, L/kg 310
57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
150
Resilience: Unit (Modulus of Resilience), kJ/m3 400
2200
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
35
Strength to Weight: Bending, points 17
28
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 15
29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.3
Carbon (C), % 0
0.16 to 0.24
Chromium (Cr), % 0
1.2 to 1.5
Copper (Cu), % 43.5 to 46.5
0
Iron (Fe), % 0
95.8 to 97.5
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0.4 to 0.8
Molybdenum (Mo), % 0
0.65 to 0.8
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0
0 to 0.035
Vanadium (V), % 0
0.25 to 0.35
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0