C79600 Nickel Silver vs. C10700 Copper

Both C79600 nickel silver and C10700 copper are copper alloys. They have 45% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is C10700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Elongation at Break, % 15
2.2 to 50
Poisson's Ratio 0.3
0.34
Shear Modulus, GPa 43
43
Shear Strength, MPa 290
160 to 240
Tensile Strength: Ultimate (UTS), MPa 480
230 to 410
Tensile Strength: Yield (Proof), MPa 300
77 to 410

Thermal Properties

Latent Heat of Fusion, J/g 180
210
Maximum Temperature: Mechanical, °C 130
200
Melting Completion (Liquidus), °C 930
1080
Melting Onset (Solidus), °C 880
1080
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 36
390
Thermal Expansion, µm/m-K 21
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
100
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
100

Otherwise Unclassified Properties

Base Metal Price, % relative 25
35
Density, g/cm3 7.9
9.0
Embodied Carbon, kg CO2/kg material 3.5
2.7
Embodied Energy, MJ/kg 57
42
Embodied Water, L/kg 310
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
7.9 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 400
25 to 710
Stiffness to Weight: Axial, points 7.8
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 17
7.2 to 13
Strength to Weight: Bending, points 17
9.4 to 14
Thermal Diffusivity, mm2/s 12
110
Thermal Shock Resistance, points 15
8.2 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 43.5 to 46.5
99.83 to 99.915
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 9.0 to 11
0
Oxygen (O), % 0
0 to 0.0010
Silver (Ag), % 0
0.085 to 0.12
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0 to 0.050