C79600 Nickel Silver vs. C66200 Brass

Both C79600 nickel silver and C66200 brass are copper alloys. They have 56% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is C66200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 15
8.0 to 15
Poisson's Ratio 0.3
0.33
Shear Modulus, GPa 43
42
Shear Strength, MPa 290
270 to 300
Tensile Strength: Ultimate (UTS), MPa 480
450 to 520
Tensile Strength: Yield (Proof), MPa 300
410 to 480

Thermal Properties

Latent Heat of Fusion, J/g 180
200
Maximum Temperature: Mechanical, °C 130
180
Melting Completion (Liquidus), °C 930
1070
Melting Onset (Solidus), °C 880
1030
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 36
150
Thermal Expansion, µm/m-K 21
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
35
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
36

Otherwise Unclassified Properties

Base Metal Price, % relative 25
29
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 3.5
2.7
Embodied Energy, MJ/kg 57
43
Embodied Water, L/kg 310
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
40 to 66
Resilience: Unit (Modulus of Resilience), kJ/m3 400
760 to 1030
Stiffness to Weight: Axial, points 7.8
7.2
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 17
14 to 17
Strength to Weight: Bending, points 17
15 to 16
Thermal Diffusivity, mm2/s 12
45
Thermal Shock Resistance, points 15
16 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 43.5 to 46.5
86.6 to 91
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0.8 to 1.2
0 to 0.050
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 9.0 to 11
0.3 to 1.0
Phosphorus (P), % 0
0.050 to 0.2
Tin (Sn), % 0
0.2 to 0.7
Zinc (Zn), % 38.3 to 45.2
6.5 to 12.9
Residuals, % 0 to 0.5
0 to 0.5