C79600 Nickel Silver vs. C92300 Bronze

Both C79600 nickel silver and C92300 bronze are copper alloys. They have 50% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is C92300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 15
19
Poisson's Ratio 0.3
0.34
Shear Modulus, GPa 43
40
Tensile Strength: Ultimate (UTS), MPa 480
300
Tensile Strength: Yield (Proof), MPa 300
140

Thermal Properties

Latent Heat of Fusion, J/g 180
190
Maximum Temperature: Mechanical, °C 130
170
Melting Completion (Liquidus), °C 930
1000
Melting Onset (Solidus), °C 880
850
Specific Heat Capacity, J/kg-K 390
370
Thermal Conductivity, W/m-K 36
75
Thermal Expansion, µm/m-K 21
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
12

Otherwise Unclassified Properties

Base Metal Price, % relative 25
33
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 3.5
3.4
Embodied Energy, MJ/kg 57
56
Embodied Water, L/kg 310
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
47
Resilience: Unit (Modulus of Resilience), kJ/m3 400
86
Stiffness to Weight: Axial, points 7.8
6.9
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 17
9.5
Strength to Weight: Bending, points 17
11
Thermal Diffusivity, mm2/s 12
23
Thermal Shock Resistance, points 15
11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 43.5 to 46.5
85 to 89
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0.8 to 1.2
0.3 to 1.0
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 9.0 to 11
0 to 1.0
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
7.5 to 9.0
Zinc (Zn), % 38.3 to 45.2
2.5 to 5.0
Residuals, % 0 to 0.5
0 to 0.7