C79600 Nickel Silver vs. S30415 Stainless Steel

C79600 nickel silver belongs to the copper alloys classification, while S30415 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C79600 nickel silver and the bottom bar is S30415 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 15
45
Poisson's Ratio 0.3
0.28
Rockwell B Hardness 70
84
Shear Modulus, GPa 43
77
Shear Strength, MPa 290
470
Tensile Strength: Ultimate (UTS), MPa 480
670
Tensile Strength: Yield (Proof), MPa 300
330

Thermal Properties

Latent Heat of Fusion, J/g 180
300
Maximum Temperature: Mechanical, °C 130
940
Melting Completion (Liquidus), °C 930
1410
Melting Onset (Solidus), °C 880
1370
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 36
21
Thermal Expansion, µm/m-K 21
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
15
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 3.5
3.1
Embodied Energy, MJ/kg 57
43
Embodied Water, L/kg 310
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63
250
Resilience: Unit (Modulus of Resilience), kJ/m3 400
280
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 12
5.6
Thermal Shock Resistance, points 15
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.040 to 0.060
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 0
18 to 19
Copper (Cu), % 43.5 to 46.5
0
Iron (Fe), % 0
67.8 to 71.8
Lead (Pb), % 0.8 to 1.2
0
Manganese (Mn), % 1.5 to 2.5
0 to 0.8
Nickel (Ni), % 9.0 to 11
9.0 to 10
Nitrogen (N), % 0
0.12 to 0.18
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
1.0 to 2.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 38.3 to 45.2
0
Residuals, % 0 to 0.5
0