C81500 Copper vs. C28000 Muntz Metal

Both C81500 copper and C28000 Muntz Metal are copper alloys. They have 61% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C81500 copper and the bottom bar is C28000 Muntz Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
100
Elongation at Break, % 17
10 to 45
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 44
40
Tensile Strength: Ultimate (UTS), MPa 350
330 to 610
Tensile Strength: Yield (Proof), MPa 280
150 to 370

Thermal Properties

Latent Heat of Fusion, J/g 210
170
Maximum Temperature: Mechanical, °C 200
120
Melting Completion (Liquidus), °C 1090
900
Melting Onset (Solidus), °C 1080
900
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 320
120
Thermal Expansion, µm/m-K 17
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 82
28
Electrical Conductivity: Equal Weight (Specific), % IACS 83
31

Otherwise Unclassified Properties

Base Metal Price, % relative 31
23
Density, g/cm3 8.9
8.0
Embodied Carbon, kg CO2/kg material 2.6
2.7
Embodied Energy, MJ/kg 41
46
Embodied Water, L/kg 310
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
27 to 240
Resilience: Unit (Modulus of Resilience), kJ/m3 330
110 to 670
Stiffness to Weight: Axial, points 7.3
7.2
Stiffness to Weight: Bending, points 18
20
Strength to Weight: Axial, points 11
11 to 21
Strength to Weight: Bending, points 12
13 to 20
Thermal Diffusivity, mm2/s 91
40
Thermal Shock Resistance, points 12
11 to 20

Alloy Composition

Aluminum (Al), % 0 to 0.1
0
Chromium (Cr), % 0.4 to 1.5
0
Copper (Cu), % 97.4 to 99.6
59 to 63
Iron (Fe), % 0 to 0.1
0 to 0.070
Lead (Pb), % 0 to 0.020
0 to 0.3
Silicon (Si), % 0 to 0.15
0
Tin (Sn), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.1
36.3 to 41
Residuals, % 0 to 0.5
0 to 0.3