C82200 Copper vs. AWS BAg-9
C82200 copper belongs to the copper alloys classification, while AWS BAg-9 belongs to the otherwise unclassified metals. They have a modest 20% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C82200 copper and the bottom bar is AWS BAg-9.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 82 |
| Poisson's Ratio | 0.34 | |
| 0.35 |
| Shear Modulus, GPa | 44 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 660 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 130 |
| Melting Completion (Liquidus), °C | 1080 | |
| 720 |
| Melting Onset (Solidus), °C | 1040 | |
| 670 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 290 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 9.6 |
| Embodied Energy, MJ/kg | 74 | |
| 980 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 4.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 15 |
| Strength to Weight: Axial, points | 12 to 20 | |
| 4.1 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 6.3 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 6.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Beryllium (Be), % | 0.35 to 0.8 | |
| 0 |
| Cobalt (Co), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 97.4 to 98.7 | |
| 19 to 21 |
| Nickel (Ni), % | 1.0 to 2.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 64 to 66 |
| Zinc (Zn), % | 0 | |
| 13 to 17 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |