C82200 Copper vs. EN 1.4923 Stainless Steel
C82200 copper belongs to the copper alloys classification, while EN 1.4923 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C82200 copper and the bottom bar is EN 1.4923 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 8.0 to 20 | |
| 12 to 21 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 44 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 660 | |
| 870 to 980 |
| Tensile Strength: Yield (Proof), MPa | 210 to 520 | |
| 470 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 740 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1450 |
| Melting Onset (Solidus), °C | 1040 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 180 | |
| 24 |
| Thermal Expansion, µm/m-K | 17 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 46 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 55 | |
| 8.0 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 2.9 |
| Embodied Energy, MJ/kg | 74 | |
| 41 |
| Embodied Water, L/kg | 310 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 49 to 66 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 1130 | |
| 570 to 1580 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 20 | |
| 31 to 35 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 26 to 28 |
| Thermal Diffusivity, mm2/s | 53 | |
| 6.5 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 30 to 34 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Beryllium (Be), % | 0.35 to 0.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.18 to 0.24 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Cobalt (Co), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 97.4 to 98.7 | |
| 0 |
| Iron (Fe), % | 0 | |
| 83.5 to 87.1 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 1.0 to 2.0 | |
| 0.3 to 0.8 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |
| Residuals, % | 0 to 0.5 | |
| 0 |