C82400 Copper vs. 354.0 Aluminum
C82400 copper belongs to the copper alloys classification, while 354.0 aluminum belongs to the aluminum alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C82400 copper and the bottom bar is 354.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 71 |
| Elongation at Break, % | 1.0 to 20 | |
| 2.4 to 3.0 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 45 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1030 | |
| 360 to 380 |
| Tensile Strength: Yield (Proof), MPa | 260 to 970 | |
| 280 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 530 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 170 |
| Melting Completion (Liquidus), °C | 1000 | |
| 600 |
| Melting Onset (Solidus), °C | 900 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 110 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 7.8 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 310 | |
| 1070 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 to 83 | |
| 8.6 to 9.8 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 3870 | |
| 540 to 670 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 52 |
| Strength to Weight: Axial, points | 16 to 33 | |
| 37 to 39 |
| Strength to Weight: Bending, points | 16 to 26 | |
| 42 to 44 |
| Thermal Diffusivity, mm2/s | 39 | |
| 52 |
| Thermal Shock Resistance, points | 17 to 36 | |
| 17 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.15 | |
| 87.3 to 89.4 |
| Beryllium (Be), % | 1.6 to 1.9 | |
| 0 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Cobalt (Co), % | 0.2 to 0.65 | |
| 0 |
| Copper (Cu), % | 96 to 98.2 | |
| 1.6 to 2.0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.4 to 0.6 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0 | |
| 8.6 to 9.4 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.12 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.15 |