C82500 Copper vs. C66300 Brass
Both C82500 copper and C66300 brass are copper alloys. They have 87% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C82500 copper and the bottom bar is C66300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 1.0 to 20 | |
| 2.3 to 22 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 45 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 1100 | |
| 460 to 810 |
| Tensile Strength: Yield (Proof), MPa | 310 to 980 | |
| 400 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 280 | |
| 180 |
| Melting Completion (Liquidus), °C | 980 | |
| 1050 |
| Melting Onset (Solidus), °C | 860 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 130 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 20 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 21 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.8 |
| Embodied Energy, MJ/kg | 160 | |
| 46 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 94 | |
| 17 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 4000 | |
| 710 to 2850 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 18 to 35 | |
| 15 to 26 |
| Strength to Weight: Bending, points | 17 to 27 | |
| 15 to 22 |
| Thermal Diffusivity, mm2/s | 38 | |
| 32 |
| Thermal Shock Resistance, points | 19 to 38 | |
| 16 to 28 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.15 | |
| 0 |
| Beryllium (Be), % | 1.9 to 2.3 | |
| 0 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Cobalt (Co), % | 0.15 to 0.7 | |
| 0 to 0.2 |
| Copper (Cu), % | 95.3 to 97.8 | |
| 84.5 to 87.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 1.4 to 2.4 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.35 |
| Silicon (Si), % | 0.2 to 0.35 | |
| 0 |
| Tin (Sn), % | 0 to 0.1 | |
| 1.5 to 3.0 |
| Titanium (Ti), % | 0 to 0.12 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 6.0 to 12.8 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |