C82500 Copper vs. Z40101 Zinc
C82500 copper belongs to the copper alloys classification, while Z40101 zinc belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C82500 copper and the bottom bar is Z40101 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 87 |
| Elongation at Break, % | 1.0 to 20 | |
| 44 |
| Poisson's Ratio | 0.33 | |
| 0.25 |
| Shear Modulus, GPa | 45 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 1100 | |
| 130 |
| Tensile Strength: Yield (Proof), MPa | 310 to 980 | |
| 110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 280 | |
| 90 |
| Melting Completion (Liquidus), °C | 980 | |
| 410 |
| Melting Onset (Solidus), °C | 860 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 130 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 20 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 21 | |
| 37 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.8 |
| Embodied Energy, MJ/kg | 160 | |
| 53 |
| Embodied Water, L/kg | 310 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 94 | |
| 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 4000 | |
| 69 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 18 to 35 | |
| 5.7 |
| Strength to Weight: Bending, points | 17 to 27 | |
| 8.9 |
| Thermal Diffusivity, mm2/s | 38 | |
| 44 |
| Thermal Shock Resistance, points | 19 to 38 | |
| 4.2 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.15 | |
| 0 to 0.010 |
| Beryllium (Be), % | 1.9 to 2.3 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Cobalt (Co), % | 0.15 to 0.7 | |
| 0 |
| Copper (Cu), % | 95.3 to 97.8 | |
| 0.080 to 0.4 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 to 0.010 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.35 | |
| 0 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 to 0.12 | |
| 0 to 0.020 |
| Zinc (Zn), % | 0 to 0.1 | |
| 99.542 to 99.92 |
| Residuals, % | 0 to 0.5 | |
| 0 |