C82800 Copper vs. S28200 Stainless Steel
C82800 copper belongs to the copper alloys classification, while S28200 stainless steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C82800 copper and the bottom bar is S28200 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 1.0 to 20 | |
| 45 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 46 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 1140 | |
| 870 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1000 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 310 | |
| 900 |
| Melting Completion (Liquidus), °C | 930 | |
| 1380 |
| Melting Onset (Solidus), °C | 890 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 12 | |
| 2.8 |
| Embodied Energy, MJ/kg | 190 | |
| 41 |
| Embodied Water, L/kg | 310 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 110 | |
| 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 590 to 4080 | |
| 540 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 26 |
| Strength to Weight: Axial, points | 21 to 36 | |
| 32 |
| Strength to Weight: Bending, points | 20 to 28 | |
| 27 |
| Thermal Shock Resistance, points | 23 to 39 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 0.15 | |
| 0 |
| Beryllium (Be), % | 2.5 to 2.9 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 to 0.1 | |
| 17 to 19 |
| Cobalt (Co), % | 0.15 to 0.7 | |
| 0 |
| Copper (Cu), % | 94.6 to 97.2 | |
| 0.75 to 1.3 |
| Iron (Fe), % | 0 to 0.25 | |
| 57.7 to 64.1 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 17 to 19 |
| Molybdenum (Mo), % | 0 | |
| 0.75 to 1.3 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.4 to 0.6 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.2 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 to 0.12 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |