C84000 Brass vs. AISI 201LN Stainless Steel

C84000 brass belongs to the copper alloys classification, while AISI 201LN stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is AISI 201LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
210 to 320
Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 27
25 to 51
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 42
77
Tensile Strength: Ultimate (UTS), MPa 250
740 to 1060
Tensile Strength: Yield (Proof), MPa 140
350 to 770

Thermal Properties

Latent Heat of Fusion, J/g 190
280
Maximum Temperature: Mechanical, °C 170
880
Melting Completion (Liquidus), °C 1040
1410
Melting Onset (Solidus), °C 940
1370
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 72
15
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 17
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
12
Density, g/cm3 8.6
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 49
38
Embodied Water, L/kg 330
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
230 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 83
310 to 1520
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 8.2
27 to 38
Strength to Weight: Bending, points 10
24 to 30
Thermal Diffusivity, mm2/s 22
4.0
Thermal Shock Resistance, points 9.0
16 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
16 to 17.5
Copper (Cu), % 82 to 89
0 to 1.0
Iron (Fe), % 0 to 0.4
67.9 to 73.5
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
6.4 to 7.5
Nickel (Ni), % 0.5 to 2.0
4.0 to 5.0
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.050
0 to 0.045
Silicon (Si), % 0 to 0.0050
0 to 0.75
Sulfur (S), % 0.1 to 0.65
0 to 0.015
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0