C84000 Brass vs. AWS E2553

C84000 brass belongs to the copper alloys classification, while AWS E2553 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is AWS E2553.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 27
17
Poisson's Ratio 0.33
0.27
Shear Modulus, GPa 42
80
Tensile Strength: Ultimate (UTS), MPa 250
850

Thermal Properties

Latent Heat of Fusion, J/g 190
300
Melting Completion (Liquidus), °C 1040
1440
Melting Onset (Solidus), °C 940
1390
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 72
16
Thermal Expansion, µm/m-K 18
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 17
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 30
21
Density, g/cm3 8.6
7.8
Embodied Carbon, kg CO2/kg material 3.0
4.0
Embodied Energy, MJ/kg 49
56
Embodied Water, L/kg 330
190

Common Calculations

Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 8.2
30
Strength to Weight: Bending, points 10
26
Thermal Diffusivity, mm2/s 22
4.3
Thermal Shock Resistance, points 9.0
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
24 to 27
Copper (Cu), % 82 to 89
1.5 to 2.5
Iron (Fe), % 0 to 0.4
55.2 to 64.5
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0.5 to 1.5
Molybdenum (Mo), % 0
2.9 to 3.9
Nickel (Ni), % 0.5 to 2.0
6.5 to 8.5
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0 to 0.050
0 to 0.040
Silicon (Si), % 0 to 0.0050
0 to 1.0
Sulfur (S), % 0.1 to 0.65
0 to 0.030
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0