C84000 Brass vs. EN 1.0214 Steel

C84000 brass belongs to the copper alloys classification, while EN 1.0214 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is EN 1.0214 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
97 to 130
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 27
12 to 31
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 42
73
Tensile Strength: Ultimate (UTS), MPa 250
330 to 460
Tensile Strength: Yield (Proof), MPa 140
210 to 360

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 170
400
Melting Completion (Liquidus), °C 1040
1470
Melting Onset (Solidus), °C 940
1420
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 72
53
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 17
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
1.8
Density, g/cm3 8.6
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 49
18
Embodied Water, L/kg 330
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
34 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 83
120 to 340
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 8.2
12 to 16
Strength to Weight: Bending, points 10
14 to 17
Thermal Diffusivity, mm2/s 22
14
Thermal Shock Resistance, points 9.0
11 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0.020 to 0.060
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0.080 to 0.12
Copper (Cu), % 82 to 89
0
Iron (Fe), % 0 to 0.4
99.17 to 99.6
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0.3 to 0.5
Nickel (Ni), % 0.5 to 2.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.025
Silicon (Si), % 0 to 0.0050
0 to 0.1
Sulfur (S), % 0.1 to 0.65
0 to 0.025
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0