C84000 Brass vs. EN 1.4373 Stainless Steel

C84000 brass belongs to the copper alloys classification, while EN 1.4373 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is EN 1.4373 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
230
Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 27
46
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 42
77
Tensile Strength: Ultimate (UTS), MPa 250
750
Tensile Strength: Yield (Proof), MPa 140
370

Thermal Properties

Latent Heat of Fusion, J/g 190
290
Maximum Temperature: Mechanical, °C 170
910
Melting Completion (Liquidus), °C 1040
1400
Melting Onset (Solidus), °C 940
1360
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 72
15
Thermal Expansion, µm/m-K 18
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 17
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 30
13
Density, g/cm3 8.6
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.8
Embodied Energy, MJ/kg 49
40
Embodied Water, L/kg 330
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
290
Resilience: Unit (Modulus of Resilience), kJ/m3 83
340
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 8.2
27
Strength to Weight: Bending, points 10
24
Thermal Diffusivity, mm2/s 22
4.0
Thermal Shock Resistance, points 9.0
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 82 to 89
0
Iron (Fe), % 0 to 0.4
63 to 71.5
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
7.5 to 10.5
Nickel (Ni), % 0.5 to 2.0
4.0 to 6.0
Nitrogen (N), % 0
0.050 to 0.25
Phosphorus (P), % 0 to 0.050
0 to 0.045
Silicon (Si), % 0 to 0.0050
0 to 1.0
Sulfur (S), % 0.1 to 0.65
0 to 0.015
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0