C84000 Brass vs. EN 1.7106 Steel

C84000 brass belongs to the copper alloys classification, while EN 1.7106 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is EN 1.7106 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
200 to 500
Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 42
72
Tensile Strength: Ultimate (UTS), MPa 250
660 to 2020

Thermal Properties

Latent Heat of Fusion, J/g 190
280
Maximum Temperature: Mechanical, °C 170
410
Melting Completion (Liquidus), °C 1040
1430
Melting Onset (Solidus), °C 940
1390
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 72
46
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 17
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.1
Density, g/cm3 8.6
7.7
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 49
20
Embodied Water, L/kg 330
47

Common Calculations

Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 8.2
24 to 73
Strength to Weight: Bending, points 10
22 to 46
Thermal Diffusivity, mm2/s 22
13
Thermal Shock Resistance, points 9.0
20 to 61

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0.52 to 0.6
Chromium (Cr), % 0
0.2 to 0.45
Copper (Cu), % 82 to 89
0
Iron (Fe), % 0 to 0.4
95.9 to 97
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0.7 to 1.0
Nickel (Ni), % 0.5 to 2.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.025
Silicon (Si), % 0 to 0.0050
1.6 to 2.0
Sulfur (S), % 0.1 to 0.65
0 to 0.025
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0