C84000 Brass vs. EN 1.7362 Steel

C84000 brass belongs to the copper alloys classification, while EN 1.7362 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is EN 1.7362 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 27
21 to 22
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 42
74
Tensile Strength: Ultimate (UTS), MPa 250
510 to 600
Tensile Strength: Yield (Proof), MPa 140
200 to 360

Thermal Properties

Latent Heat of Fusion, J/g 190
260
Maximum Temperature: Mechanical, °C 170
510
Melting Completion (Liquidus), °C 1040
1460
Melting Onset (Solidus), °C 940
1420
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 72
40
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 17
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 30
4.5
Density, g/cm3 8.6
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.8
Embodied Energy, MJ/kg 49
23
Embodied Water, L/kg 330
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 83
100 to 340
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 8.2
18 to 21
Strength to Weight: Bending, points 10
18 to 20
Thermal Diffusivity, mm2/s 22
11
Thermal Shock Resistance, points 9.0
14 to 17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0.1 to 0.15
Chromium (Cr), % 0
4.0 to 6.0
Copper (Cu), % 82 to 89
0 to 0.3
Iron (Fe), % 0 to 0.4
91.5 to 95.2
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0.3 to 0.6
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 0.5 to 2.0
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.050
0 to 0.020
Silicon (Si), % 0 to 0.0050
0 to 0.5
Sulfur (S), % 0.1 to 0.65
0 to 0.0050
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0