C84000 Brass vs. CC754S Brass

Both C84000 brass and CC754S brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 71% of their average alloy composition in common.

For each property being compared, the top bar is C84000 brass and the bottom bar is CC754S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
90
Elastic (Young's, Tensile) Modulus, GPa 110
100
Elongation at Break, % 27
11
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 42
40
Tensile Strength: Ultimate (UTS), MPa 250
320
Tensile Strength: Yield (Proof), MPa 140
160

Thermal Properties

Latent Heat of Fusion, J/g 190
170
Maximum Temperature: Mechanical, °C 170
120
Melting Completion (Liquidus), °C 1040
830
Melting Onset (Solidus), °C 940
780
Specific Heat Capacity, J/kg-K 380
390
Thermal Conductivity, W/m-K 72
95
Thermal Expansion, µm/m-K 18
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
27
Electrical Conductivity: Equal Weight (Specific), % IACS 17
30

Otherwise Unclassified Properties

Base Metal Price, % relative 30
23
Density, g/cm3 8.6
8.1
Embodied Carbon, kg CO2/kg material 3.0
2.8
Embodied Energy, MJ/kg 49
47
Embodied Water, L/kg 330
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
29
Resilience: Unit (Modulus of Resilience), kJ/m3 83
130
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 19
19
Strength to Weight: Axial, points 8.2
11
Strength to Weight: Bending, points 10
13
Thermal Diffusivity, mm2/s 22
31
Thermal Shock Resistance, points 9.0
10

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0 to 0.8
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Copper (Cu), % 82 to 89
57 to 63
Iron (Fe), % 0 to 0.4
0 to 0.7
Lead (Pb), % 0 to 0.090
0.5 to 2.5
Manganese (Mn), % 0 to 0.010
0 to 0.5
Nickel (Ni), % 0.5 to 2.0
0 to 1.0
Phosphorus (P), % 0 to 0.050
0 to 0.020
Silicon (Si), % 0 to 0.0050
0 to 0.3
Sulfur (S), % 0.1 to 0.65
0
Tin (Sn), % 2.0 to 4.0
0 to 1.0
Zinc (Zn), % 5.0 to 14
30.2 to 42.5
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0