C84000 Brass vs. Grade N12MV Nickel

C84000 brass belongs to the copper alloys classification, while grade N12MV nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is grade N12MV nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
220
Elongation at Break, % 27
6.8
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 42
84
Tensile Strength: Ultimate (UTS), MPa 250
600
Tensile Strength: Yield (Proof), MPa 140
310

Thermal Properties

Latent Heat of Fusion, J/g 190
320
Maximum Temperature: Mechanical, °C 170
900
Melting Completion (Liquidus), °C 1040
1620
Melting Onset (Solidus), °C 940
1570
Specific Heat Capacity, J/kg-K 380
390
Thermal Expansion, µm/m-K 18
10

Otherwise Unclassified Properties

Base Metal Price, % relative 30
75
Density, g/cm3 8.6
9.2
Embodied Carbon, kg CO2/kg material 3.0
16
Embodied Energy, MJ/kg 49
200
Embodied Water, L/kg 330
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
34
Resilience: Unit (Modulus of Resilience), kJ/m3 83
220
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
22
Strength to Weight: Axial, points 8.2
18
Strength to Weight: Bending, points 10
17
Thermal Shock Resistance, points 9.0
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
0 to 1.0
Copper (Cu), % 82 to 89
0
Iron (Fe), % 0 to 0.4
4.0 to 6.0
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0 to 1.0
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0.5 to 2.0
60.2 to 69.8
Phosphorus (P), % 0 to 0.050
0 to 0.040
Silicon (Si), % 0 to 0.0050
0 to 1.0
Sulfur (S), % 0.1 to 0.65
0 to 0.030
Tin (Sn), % 2.0 to 4.0
0
Vanadium (V), % 0
0.2 to 0.6
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0