MakeItFrom.com
Menu (ESC)

C84000 Brass vs. SAE-AISI 5155 Steel

C84000 brass belongs to the copper alloys classification, while SAE-AISI 5155 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is SAE-AISI 5155 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 65
190
Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 27
21
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 42
73
Tensile Strength: Ultimate (UTS), MPa 250
620
Tensile Strength: Yield (Proof), MPa 140
380

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 170
420
Melting Completion (Liquidus), °C 1040
1450
Melting Onset (Solidus), °C 940
1410
Specific Heat Capacity, J/kg-K 380
470
Thermal Conductivity, W/m-K 72
49
Thermal Expansion, µm/m-K 18
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 16
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 17
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.1
Density, g/cm3 8.6
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 49
19
Embodied Water, L/kg 330
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
110
Resilience: Unit (Modulus of Resilience), kJ/m3 83
380
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 8.2
22
Strength to Weight: Bending, points 10
21
Thermal Diffusivity, mm2/s 22
13
Thermal Shock Resistance, points 9.0
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0.51 to 0.59
Chromium (Cr), % 0
0.7 to 0.9
Copper (Cu), % 82 to 89
0
Iron (Fe), % 0 to 0.4
97.2 to 97.9
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0.7 to 0.9
Nickel (Ni), % 0.5 to 2.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.035
Silicon (Si), % 0 to 0.0050
0.15 to 0.35
Sulfur (S), % 0.1 to 0.65
0 to 0.040
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0