C84000 Brass vs. N06045 Nickel

C84000 brass belongs to the copper alloys classification, while N06045 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is N06045 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 27
37
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 42
77
Tensile Strength: Ultimate (UTS), MPa 250
690
Tensile Strength: Yield (Proof), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 190
350
Maximum Temperature: Mechanical, °C 170
1010
Melting Completion (Liquidus), °C 1040
1350
Melting Onset (Solidus), °C 940
1300
Specific Heat Capacity, J/kg-K 380
480
Thermal Expansion, µm/m-K 18
13

Otherwise Unclassified Properties

Base Metal Price, % relative 30
42
Density, g/cm3 8.6
8.0
Embodied Carbon, kg CO2/kg material 3.0
6.9
Embodied Energy, MJ/kg 49
98
Embodied Water, L/kg 330
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
200
Resilience: Unit (Modulus of Resilience), kJ/m3 83
180
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 8.2
24
Strength to Weight: Bending, points 10
22
Thermal Shock Resistance, points 9.0
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 0
26 to 29
Copper (Cu), % 82 to 89
0 to 0.3
Iron (Fe), % 0 to 0.4
21 to 25
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0 to 1.0
Nickel (Ni), % 0.5 to 2.0
45 to 50.4
Phosphorus (P), % 0 to 0.050
0 to 0.020
Silicon (Si), % 0 to 0.0050
2.5 to 3.0
Sulfur (S), % 0.1 to 0.65
0 to 0.010
Tin (Sn), % 2.0 to 4.0
0
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0