C84000 Brass vs. N06250 Nickel

C84000 brass belongs to the copper alloys classification, while N06250 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C84000 brass and the bottom bar is N06250 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
210
Elongation at Break, % 27
46
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 42
82
Tensile Strength: Ultimate (UTS), MPa 250
710
Tensile Strength: Yield (Proof), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 190
320
Maximum Temperature: Mechanical, °C 170
980
Melting Completion (Liquidus), °C 1040
1490
Melting Onset (Solidus), °C 940
1440
Specific Heat Capacity, J/kg-K 380
440
Thermal Expansion, µm/m-K 18
13

Otherwise Unclassified Properties

Base Metal Price, % relative 30
55
Density, g/cm3 8.6
8.6
Embodied Carbon, kg CO2/kg material 3.0
10
Embodied Energy, MJ/kg 49
140
Embodied Water, L/kg 330
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 58
260
Resilience: Unit (Modulus of Resilience), kJ/m3 83
170
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 19
23
Strength to Weight: Axial, points 8.2
23
Strength to Weight: Bending, points 10
21
Thermal Shock Resistance, points 9.0
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0 to 0.0050
0
Antimony (Sb), % 0 to 0.020
0
Boron (B), % 0 to 0.1
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
20 to 23
Copper (Cu), % 82 to 89
0.25 to 1.3
Iron (Fe), % 0 to 0.4
7.4 to 19.4
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0 to 0.010
0 to 1.0
Molybdenum (Mo), % 0
10.1 to 12
Nickel (Ni), % 0.5 to 2.0
50 to 54
Phosphorus (P), % 0 to 0.050
0 to 0.030
Silicon (Si), % 0 to 0.0050
0 to 0.090
Sulfur (S), % 0.1 to 0.65
0 to 0.0050
Tin (Sn), % 2.0 to 4.0
0
Tungsten (W), % 0
0.25 to 1.3
Zinc (Zn), % 5.0 to 14
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.7
0