C85900 Brass vs. Grade M30H Nickel
C85900 brass belongs to the copper alloys classification, while grade M30H nickel belongs to the nickel alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C85900 brass and the bottom bar is grade M30H nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 160 |
| Elongation at Break, % | 30 | |
| 11 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 61 |
| Tensile Strength: Ultimate (UTS), MPa | 460 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 900 |
| Melting Completion (Liquidus), °C | 830 | |
| 1250 |
| Melting Onset (Solidus), °C | 790 | |
| 1200 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Conductivity, W/m-K | 89 | |
| 22 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 50 |
| Density, g/cm3 | 8.0 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 7.7 |
| Embodied Energy, MJ/kg | 49 | |
| 110 |
| Embodied Water, L/kg | 330 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 75 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 700 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 10 |
| Stiffness to Weight: Bending, points | 20 | |
| 21 |
| Strength to Weight: Axial, points | 16 | |
| 25 |
| Strength to Weight: Bending, points | 17 | |
| 22 |
| Thermal Diffusivity, mm2/s | 29 | |
| 5.7 |
| Thermal Shock Resistance, points | 16 | |
| 27 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.1 to 0.6 | |
| 0 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Boron (B), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 58 to 62 | |
| 27 to 33 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 3.5 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 to 1.5 | |
| 57.9 to 70.3 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.25 | |
| 2.7 to 3.7 |
| Sulfur (S), % | 0.1 to 0.65 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 1.5 | |
| 0 |
| Zinc (Zn), % | 31 to 41 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.7 | |
| 0 |