C86300 Bronze vs. 1350 Aluminum

C86300 bronze belongs to the copper alloys classification, while 1350 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C86300 bronze and the bottom bar is 1350 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
20 to 45
Elastic (Young's, Tensile) Modulus, GPa 110
68
Elongation at Break, % 14
1.4 to 30
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 42
26
Tensile Strength: Ultimate (UTS), MPa 850
68 to 190
Tensile Strength: Yield (Proof), MPa 480
25 to 170

Thermal Properties

Latent Heat of Fusion, J/g 200
400
Maximum Temperature: Mechanical, °C 160
170
Melting Completion (Liquidus), °C 920
660
Melting Onset (Solidus), °C 890
650
Specific Heat Capacity, J/kg-K 420
900
Thermal Conductivity, W/m-K 35
230
Thermal Expansion, µm/m-K 20
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
61 to 62
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
200 to 210

Otherwise Unclassified Properties

Base Metal Price, % relative 23
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 3.0
8.3
Embodied Energy, MJ/kg 51
160
Embodied Water, L/kg 360
1200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
0.77 to 54
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
4.4 to 200
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
50
Strength to Weight: Axial, points 30
7.0 to 19
Strength to Weight: Bending, points 25
14 to 27
Thermal Diffusivity, mm2/s 11
96
Thermal Shock Resistance, points 28
3.0 to 8.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
99.5 to 100
Boron (B), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.010
Copper (Cu), % 60 to 66
0 to 0.050
Gallium (Ga), % 0
0 to 0.030
Iron (Fe), % 2.0 to 4.0
0 to 0.4
Lead (Pb), % 0 to 0.2
0
Manganese (Mn), % 2.5 to 5.0
0 to 0.010
Nickel (Ni), % 0 to 1.0
0
Silicon (Si), % 0
0 to 0.1
Tin (Sn), % 0 to 0.2
0
Titanium (Ti), % 0
0 to 0.020
Vanadium (V), % 0
0 to 0.020
Zinc (Zn), % 22 to 28
0 to 0.050
Residuals, % 0 to 1.0
0 to 0.1