C86300 Bronze vs. 2219 Aluminum

C86300 bronze belongs to the copper alloys classification, while 2219 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C86300 bronze and the bottom bar is 2219 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
72
Elongation at Break, % 14
2.2 to 20
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 42
27
Tensile Strength: Ultimate (UTS), MPa 850
180 to 480
Tensile Strength: Yield (Proof), MPa 480
88 to 390

Thermal Properties

Latent Heat of Fusion, J/g 200
390
Maximum Temperature: Mechanical, °C 160
230
Melting Completion (Liquidus), °C 920
640
Melting Onset (Solidus), °C 890
540
Specific Heat Capacity, J/kg-K 420
870
Thermal Conductivity, W/m-K 35
110 to 170
Thermal Expansion, µm/m-K 20
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
28 to 44
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
81 to 130

Otherwise Unclassified Properties

Base Metal Price, % relative 23
11
Density, g/cm3 7.8
3.1
Embodied Carbon, kg CO2/kg material 3.0
8.2
Embodied Energy, MJ/kg 51
150
Embodied Water, L/kg 360
1130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
9.6 to 60
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
54 to 1060
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
44
Strength to Weight: Axial, points 30
16 to 43
Strength to Weight: Bending, points 25
23 to 44
Thermal Diffusivity, mm2/s 11
42 to 63
Thermal Shock Resistance, points 28
8.2 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
91.5 to 93.8
Copper (Cu), % 60 to 66
5.8 to 6.8
Iron (Fe), % 2.0 to 4.0
0 to 0.3
Lead (Pb), % 0 to 0.2
0
Magnesium (Mg), % 0
0 to 0.020
Manganese (Mn), % 2.5 to 5.0
0.2 to 0.4
Nickel (Ni), % 0 to 1.0
0
Silicon (Si), % 0
0 to 0.2
Tin (Sn), % 0 to 0.2
0
Titanium (Ti), % 0
0.020 to 0.1
Vanadium (V), % 0
0.050 to 0.15
Zinc (Zn), % 22 to 28
0 to 0.1
Zirconium (Zr), % 0
0.1 to 0.25
Residuals, % 0 to 1.0
0 to 0.15