C86300 Bronze vs. 5154 Aluminum

C86300 bronze belongs to the copper alloys classification, while 5154 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C86300 bronze and the bottom bar is 5154 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
68
Elongation at Break, % 14
3.4 to 20
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 42
26
Tensile Strength: Ultimate (UTS), MPa 850
240 to 360
Tensile Strength: Yield (Proof), MPa 480
94 to 270

Thermal Properties

Latent Heat of Fusion, J/g 200
400
Maximum Temperature: Mechanical, °C 160
190
Melting Completion (Liquidus), °C 920
640
Melting Onset (Solidus), °C 890
590
Specific Heat Capacity, J/kg-K 420
900
Thermal Conductivity, W/m-K 35
130
Thermal Expansion, µm/m-K 20
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
32
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
110

Otherwise Unclassified Properties

Base Metal Price, % relative 23
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 3.0
8.8
Embodied Energy, MJ/kg 51
150
Embodied Water, L/kg 360
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
11 to 39
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
64 to 540
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
51
Strength to Weight: Axial, points 30
25 to 37
Strength to Weight: Bending, points 25
32 to 42
Thermal Diffusivity, mm2/s 11
52
Thermal Shock Resistance, points 28
10 to 16

Alloy Composition

Aluminum (Al), % 5.0 to 7.5
94.4 to 96.8
Chromium (Cr), % 0
0.15 to 0.35
Copper (Cu), % 60 to 66
0 to 0.1
Iron (Fe), % 2.0 to 4.0
0 to 0.4
Lead (Pb), % 0 to 0.2
0
Magnesium (Mg), % 0
3.1 to 3.9
Manganese (Mn), % 2.5 to 5.0
0 to 0.1
Nickel (Ni), % 0 to 1.0
0
Silicon (Si), % 0
0 to 0.25
Tin (Sn), % 0 to 0.2
0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 22 to 28
0 to 0.2
Residuals, % 0 to 1.0
0 to 0.15