C86300 Bronze vs. 6105 Aluminum

C86300 bronze belongs to the copper alloys classification, while 6105 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C86300 bronze and the bottom bar is 6105 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
68
Elongation at Break, % 14
9.0 to 16
Poisson's Ratio 0.32
0.33
Shear Modulus, GPa 42
26
Tensile Strength: Ultimate (UTS), MPa 850
190 to 280
Tensile Strength: Yield (Proof), MPa 480
120 to 270

Thermal Properties

Latent Heat of Fusion, J/g 200
410
Maximum Temperature: Mechanical, °C 160
160
Melting Completion (Liquidus), °C 920
650
Melting Onset (Solidus), °C 890
600
Specific Heat Capacity, J/kg-K 420
900
Thermal Conductivity, W/m-K 35
180 to 190
Thermal Expansion, µm/m-K 20
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
46 to 50
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
150 to 170

Otherwise Unclassified Properties

Base Metal Price, % relative 23
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 3.0
8.3
Embodied Energy, MJ/kg 51
150
Embodied Water, L/kg 360
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
25 to 27
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
100 to 550
Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
51
Strength to Weight: Axial, points 30
20 to 29
Strength to Weight: Bending, points 25
28 to 35
Thermal Diffusivity, mm2/s 11
72 to 79
Thermal Shock Resistance, points 28
8.6 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
97.2 to 99
Chromium (Cr), % 0
0 to 0.1
Copper (Cu), % 60 to 66
0 to 0.1
Iron (Fe), % 2.0 to 4.0
0 to 0.35
Lead (Pb), % 0 to 0.2
0
Magnesium (Mg), % 0
0.45 to 0.8
Manganese (Mn), % 2.5 to 5.0
0 to 0.1
Nickel (Ni), % 0 to 1.0
0
Silicon (Si), % 0
0.6 to 1.0
Tin (Sn), % 0 to 0.2
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 22 to 28
0 to 0.1
Residuals, % 0 to 1.0
0 to 0.15