C86300 Bronze vs. 713.0 Aluminum

C86300 bronze belongs to the copper alloys classification, while 713.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C86300 bronze and the bottom bar is 713.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
74 to 75
Elastic (Young's, Tensile) Modulus, GPa 110
71
Elongation at Break, % 14
3.9 to 4.3
Poisson's Ratio 0.32
0.32
Shear Modulus, GPa 42
27
Tensile Strength: Ultimate (UTS), MPa 850
240 to 260
Tensile Strength: Yield (Proof), MPa 480
170

Thermal Properties

Latent Heat of Fusion, J/g 200
370
Maximum Temperature: Mechanical, °C 160
180
Melting Completion (Liquidus), °C 920
630
Melting Onset (Solidus), °C 890
610
Specific Heat Capacity, J/kg-K 420
860
Thermal Conductivity, W/m-K 35
150
Thermal Expansion, µm/m-K 20
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
35
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
100

Otherwise Unclassified Properties

Base Metal Price, % relative 23
9.5
Density, g/cm3 7.8
3.1
Embodied Carbon, kg CO2/kg material 3.0
7.8
Embodied Energy, MJ/kg 51
150
Embodied Water, L/kg 360
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
8.7 to 9.9
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
210 to 220
Stiffness to Weight: Axial, points 7.8
13
Stiffness to Weight: Bending, points 20
45
Strength to Weight: Axial, points 30
22 to 23
Strength to Weight: Bending, points 25
28 to 29
Thermal Diffusivity, mm2/s 11
57
Thermal Shock Resistance, points 28
10 to 11

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
87.6 to 92.4
Chromium (Cr), % 0
0 to 0.35
Copper (Cu), % 60 to 66
0.4 to 1.0
Iron (Fe), % 2.0 to 4.0
0 to 1.1
Lead (Pb), % 0 to 0.2
0
Magnesium (Mg), % 0
0.2 to 0.5
Manganese (Mn), % 2.5 to 5.0
0 to 0.6
Nickel (Ni), % 0 to 1.0
0 to 0.15
Silicon (Si), % 0
0 to 0.25
Tin (Sn), % 0 to 0.2
0
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 22 to 28
7.0 to 8.0
Residuals, % 0 to 1.0
0 to 0.25