C86300 Bronze vs. AISI 440B Stainless Steel
C86300 bronze belongs to the copper alloys classification, while AISI 440B stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C86300 bronze and the bottom bar is AISI 440B stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 14 | |
| 3.0 to 18 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 740 to 1930 |
| Tensile Strength: Yield (Proof), MPa | 480 | |
| 430 to 1860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 870 |
| Melting Completion (Liquidus), °C | 920 | |
| 1480 |
| Melting Onset (Solidus), °C | 890 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 480 |
| Thermal Conductivity, W/m-K | 35 | |
| 23 |
| Thermal Expansion, µm/m-K | 20 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 9.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.2 |
| Embodied Energy, MJ/kg | 51 | |
| 31 |
| Embodied Water, L/kg | 360 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 57 to 110 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 30 | |
| 27 to 70 |
| Strength to Weight: Bending, points | 25 | |
| 24 to 45 |
| Thermal Diffusivity, mm2/s | 11 | |
| 6.1 |
| Thermal Shock Resistance, points | 28 | |
| 27 to 70 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 5.0 to 7.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.75 to 1.0 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Copper (Cu), % | 60 to 66 | |
| 0 |
| Iron (Fe), % | 2.0 to 4.0 | |
| 78.2 to 83.3 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 2.5 to 5.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 22 to 28 | |
| 0 |
| Residuals, % | 0 to 1.0 | |
| 0 |