C86300 Bronze vs. CC755S Brass

Both C86300 bronze and CC755S brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 86% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is C86300 bronze and the bottom bar is CC755S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
110
Elastic (Young's, Tensile) Modulus, GPa 110
100
Elongation at Break, % 14
9.5
Poisson's Ratio 0.32
0.31
Shear Modulus, GPa 42
40
Tensile Strength: Ultimate (UTS), MPa 850
390
Tensile Strength: Yield (Proof), MPa 480
250

Thermal Properties

Latent Heat of Fusion, J/g 200
170
Maximum Temperature: Mechanical, °C 160
120
Melting Completion (Liquidus), °C 920
820
Melting Onset (Solidus), °C 890
780
Specific Heat Capacity, J/kg-K 420
390
Thermal Conductivity, W/m-K 35
120
Thermal Expansion, µm/m-K 20
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
27
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
30

Otherwise Unclassified Properties

Base Metal Price, % relative 23
23
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.0
2.7
Embodied Energy, MJ/kg 51
46
Embodied Water, L/kg 360
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
33
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
290
Stiffness to Weight: Axial, points 7.8
7.1
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 30
14
Strength to Weight: Bending, points 25
15
Thermal Diffusivity, mm2/s 11
38
Thermal Shock Resistance, points 28
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
0.4 to 0.7
Copper (Cu), % 60 to 66
59.5 to 61
Iron (Fe), % 2.0 to 4.0
0.050 to 0.2
Lead (Pb), % 0 to 0.2
1.2 to 1.7
Manganese (Mn), % 2.5 to 5.0
0 to 0.050
Nickel (Ni), % 0 to 1.0
0 to 0.2
Silicon (Si), % 0
0 to 0.050
Tin (Sn), % 0 to 0.2
0 to 0.3
Zinc (Zn), % 22 to 28
35.8 to 38.9
Residuals, % 0 to 1.0
0