C86300 Bronze vs. CR016A Copper

Both C86300 bronze and CR016A copper are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 63% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C86300 bronze and the bottom bar is CR016A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
120
Elongation at Break, % 14
15
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 42
43
Tensile Strength: Ultimate (UTS), MPa 850
230
Tensile Strength: Yield (Proof), MPa 480
140

Thermal Properties

Latent Heat of Fusion, J/g 200
210
Maximum Temperature: Mechanical, °C 160
200
Melting Completion (Liquidus), °C 920
1090
Melting Onset (Solidus), °C 890
1040
Specific Heat Capacity, J/kg-K 420
390
Thermal Conductivity, W/m-K 35
390
Thermal Expansion, µm/m-K 20
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
98
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
99

Otherwise Unclassified Properties

Base Metal Price, % relative 23
35
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 3.0
2.7
Embodied Energy, MJ/kg 51
42
Embodied Water, L/kg 360
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
31
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
83
Stiffness to Weight: Axial, points 7.8
7.2
Stiffness to Weight: Bending, points 20
18
Strength to Weight: Axial, points 30
7.1
Strength to Weight: Bending, points 25
9.3
Thermal Diffusivity, mm2/s 11
110
Thermal Shock Resistance, points 28
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
0
Bismuth (Bi), % 0
0 to 0.00050
Copper (Cu), % 60 to 66
99.843 to 99.919
Iron (Fe), % 2.0 to 4.0
0
Lead (Pb), % 0 to 0.2
0
Manganese (Mn), % 2.5 to 5.0
0
Nickel (Ni), % 0 to 1.0
0
Phosphorus (P), % 0
0.0010 to 0.0070
Silver (Ag), % 0
0.080 to 0.12
Tin (Sn), % 0 to 0.2
0
Zinc (Zn), % 22 to 28
0
Residuals, % 0 to 1.0
0