C86300 Bronze vs. C86400 Bronze

Both C86300 bronze and C86400 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 88% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C86300 bronze and the bottom bar is C86400 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
100
Elongation at Break, % 14
17
Poisson's Ratio 0.32
0.31
Shear Modulus, GPa 42
40
Tensile Strength: Ultimate (UTS), MPa 850
470
Tensile Strength: Yield (Proof), MPa 480
150

Thermal Properties

Latent Heat of Fusion, J/g 200
170
Maximum Temperature: Mechanical, °C 160
120
Melting Completion (Liquidus), °C 920
880
Melting Onset (Solidus), °C 890
860
Specific Heat Capacity, J/kg-K 420
390
Thermal Conductivity, W/m-K 35
88
Thermal Expansion, µm/m-K 20
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
19
Electrical Conductivity: Equal Weight (Specific), % IACS 9.2
22

Otherwise Unclassified Properties

Base Metal Price, % relative 23
23
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
2.8
Embodied Energy, MJ/kg 51
48
Embodied Water, L/kg 360
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
63
Resilience: Unit (Modulus of Resilience), kJ/m3 1030
110
Stiffness to Weight: Axial, points 7.8
7.3
Stiffness to Weight: Bending, points 20
20
Strength to Weight: Axial, points 30
16
Strength to Weight: Bending, points 25
17
Thermal Diffusivity, mm2/s 11
29
Thermal Shock Resistance, points 28
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 5.0 to 7.5
0.5 to 1.5
Copper (Cu), % 60 to 66
56 to 62
Iron (Fe), % 2.0 to 4.0
0.4 to 2.0
Lead (Pb), % 0 to 0.2
0.5 to 1.5
Manganese (Mn), % 2.5 to 5.0
0.1 to 1.0
Nickel (Ni), % 0 to 1.0
0 to 1.0
Tin (Sn), % 0 to 0.2
0.5 to 1.5
Zinc (Zn), % 22 to 28
34 to 42
Residuals, % 0 to 1.0
0 to 1.0