C86400 Bronze vs. C96600 Copper
Both C86400 bronze and C96600 copper are copper alloys. They have 61% of their average alloy composition in common.
For each property being compared, the top bar is C86400 bronze and the bottom bar is C96600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 140 |
| Elongation at Break, % | 17 | |
| 7.0 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 760 |
| Tensile Strength: Yield (Proof), MPa | 150 | |
| 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 280 |
| Melting Completion (Liquidus), °C | 880 | |
| 1180 |
| Melting Onset (Solidus), °C | 860 | |
| 1100 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 88 | |
| 30 |
| Thermal Expansion, µm/m-K | 21 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 19 | |
| 4.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 22 | |
| 4.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 65 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 7.0 |
| Embodied Energy, MJ/kg | 48 | |
| 100 |
| Embodied Water, L/kg | 330 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 | |
| 47 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
| 830 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 8.7 |
| Stiffness to Weight: Bending, points | 20 | |
| 20 |
| Strength to Weight: Axial, points | 16 | |
| 24 |
| Strength to Weight: Bending, points | 17 | |
| 21 |
| Thermal Diffusivity, mm2/s | 29 | |
| 8.4 |
| Thermal Shock Resistance, points | 16 | |
| 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0.5 to 1.5 | |
| 0 |
| Beryllium (Be), % | 0 | |
| 0.4 to 0.7 |
| Copper (Cu), % | 56 to 62 | |
| 63.5 to 69.8 |
| Iron (Fe), % | 0.4 to 2.0 | |
| 0.8 to 1.1 |
| Lead (Pb), % | 0.5 to 1.5 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.1 to 1.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 29 to 33 |
| Silicon (Si), % | 0 | |
| 0 to 0.15 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Zinc (Zn), % | 34 to 42 | |
| 0 |
| Residuals, % | 0 to 1.0 | |
| 0 to 0.5 |