C86800 Bronze vs. C10500 Copper
Both C86800 bronze and C10500 copper are copper alloys. They have 55% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C86800 bronze and the bottom bar is C10500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 22 | |
| 2.8 to 51 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 220 to 400 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 75 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 200 |
| Melting Completion (Liquidus), °C | 900 | |
| 1080 |
| Melting Onset (Solidus), °C | 880 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 32 |
| Density, g/cm3 | 7.9 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 51 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 11 to 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 | |
| 24 to 680 |
| Stiffness to Weight: Axial, points | 7.7 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 20 | |
| 6.8 to 12 |
| Strength to Weight: Bending, points | 19 | |
| 9.1 to 14 |
| Thermal Shock Resistance, points | 18 | |
| 7.8 to 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 to 2.0 | |
| 0 |
| Copper (Cu), % | 53.5 to 57 | |
| 99.89 to 99.966 |
| Iron (Fe), % | 1.0 to 2.5 | |
| 0 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 2.5 to 4.0 | |
| 0 |
| Nickel (Ni), % | 2.5 to 4.0 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0010 |
| Silver (Ag), % | 0 | |
| 0.034 to 0.060 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Zinc (Zn), % | 28.3 to 40.5 | |
| 0 |
| Residuals, % | 0 to 1.0 | |
| 0 to 0.050 |