C87300 Bronze vs. CR008A Copper
Both C87300 bronze and CR008A copper are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a moderately high 95% of their average alloy composition in common.
For each property being compared, the top bar is C87300 bronze and the bottom bar is CR008A copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 22 | |
| 15 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 970 | |
| 1090 |
| Melting Onset (Solidus), °C | 820 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 390 |
| Thermal Conductivity, W/m-K | 28 | |
| 380 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.1 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.4 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 31 |
| Density, g/cm3 | 8.6 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 42 | |
| 41 |
| Embodied Water, L/kg | 300 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 | |
| 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 86 | |
| 76 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 | |
| 6.8 |
| Strength to Weight: Bending, points | 13 | |
| 9.0 |
| Thermal Diffusivity, mm2/s | 8.0 | |
| 110 |
| Thermal Shock Resistance, points | 13 | |
| 7.8 |
Alloy Composition
| Bismuth (Bi), % | 0 | |
| 0 to 0.00050 |
| Copper (Cu), % | 94 to 95.7 | |
| 99.95 to 100 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 to 0.0050 |
| Manganese (Mn), % | 0.8 to 1.5 | |
| 0 |
| Silicon (Si), % | 3.5 to 5.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |