C87900 Brass vs. 5449 Aluminum

C87900 brass belongs to the copper alloys classification, while 5449 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C87900 brass and the bottom bar is 5449 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
69
Elongation at Break, % 25
4.0 to 17
Poisson's Ratio 0.31
0.33
Shear Modulus, GPa 41
26
Tensile Strength: Ultimate (UTS), MPa 480
210 to 330
Tensile Strength: Yield (Proof), MPa 240
91 to 260

Thermal Properties

Latent Heat of Fusion, J/g 190
400
Maximum Temperature: Mechanical, °C 130
190
Melting Completion (Liquidus), °C 930
650
Melting Onset (Solidus), °C 900
590
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 120
140
Thermal Expansion, µm/m-K 20
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
35
Electrical Conductivity: Equal Weight (Specific), % IACS 17
110

Otherwise Unclassified Properties

Base Metal Price, % relative 24
9.5
Density, g/cm3 8.1
2.8
Embodied Carbon, kg CO2/kg material 2.7
8.5
Embodied Energy, MJ/kg 46
150
Embodied Water, L/kg 320
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
12 to 29
Resilience: Unit (Modulus of Resilience), kJ/m3 270
60 to 480
Stiffness to Weight: Axial, points 7.3
14
Stiffness to Weight: Bending, points 20
50
Strength to Weight: Axial, points 17
22 to 33
Strength to Weight: Bending, points 17
29 to 39
Thermal Diffusivity, mm2/s 37
56
Thermal Shock Resistance, points 16
9.4 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.15
94.1 to 97.8
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 63 to 69.2
0 to 0.3
Iron (Fe), % 0 to 0.4
0 to 0.7
Lead (Pb), % 0 to 0.25
0
Magnesium (Mg), % 0
1.6 to 2.6
Manganese (Mn), % 0 to 0.15
0.6 to 1.1
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0.8 to 1.2
0 to 0.4
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0 to 0.25
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 30 to 36
0 to 0.3
Residuals, % 0
0 to 0.15