C87900 Brass vs. 6463 Aluminum

C87900 brass belongs to the copper alloys classification, while 6463 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C87900 brass and the bottom bar is 6463 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
68
Elongation at Break, % 25
9.0 to 17
Poisson's Ratio 0.31
0.33
Shear Modulus, GPa 41
26
Tensile Strength: Ultimate (UTS), MPa 480
140 to 230
Tensile Strength: Yield (Proof), MPa 240
82 to 200

Thermal Properties

Latent Heat of Fusion, J/g 190
400
Maximum Temperature: Mechanical, °C 130
160
Melting Completion (Liquidus), °C 930
660
Melting Onset (Solidus), °C 900
620
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 120
190 to 210
Thermal Expansion, µm/m-K 20
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
50 to 55
Electrical Conductivity: Equal Weight (Specific), % IACS 17
170 to 180

Otherwise Unclassified Properties

Base Metal Price, % relative 24
9.5
Density, g/cm3 8.1
2.7
Embodied Carbon, kg CO2/kg material 2.7
8.3
Embodied Energy, MJ/kg 46
150
Embodied Water, L/kg 320
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
17 to 25
Resilience: Unit (Modulus of Resilience), kJ/m3 270
50 to 300
Stiffness to Weight: Axial, points 7.3
14
Stiffness to Weight: Bending, points 20
50
Strength to Weight: Axial, points 17
14 to 24
Strength to Weight: Bending, points 17
22 to 31
Thermal Diffusivity, mm2/s 37
79 to 86
Thermal Shock Resistance, points 16
6.3 to 10

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.15
97.9 to 99.4
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Copper (Cu), % 63 to 69.2
0 to 0.2
Iron (Fe), % 0 to 0.4
0 to 0.15
Lead (Pb), % 0 to 0.25
0
Magnesium (Mg), % 0
0.45 to 0.9
Manganese (Mn), % 0 to 0.15
0 to 0.050
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0.8 to 1.2
0.2 to 0.6
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 30 to 36
0 to 0.050
Residuals, % 0
0 to 0.15