C87900 Brass vs. AWS BAg-35

C87900 brass belongs to the copper alloys classification, while AWS BAg-35 belongs to the otherwise unclassified metals. They have 65% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is AWS BAg-35.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
91
Poisson's Ratio 0.31
0.32
Shear Modulus, GPa 41
34
Tensile Strength: Ultimate (UTS), MPa 480
170

Thermal Properties

Latent Heat of Fusion, J/g 190
140
Melting Completion (Liquidus), °C 930
750
Melting Onset (Solidus), °C 900
690
Specific Heat Capacity, J/kg-K 390
330
Thermal Expansion, µm/m-K 20
21

Otherwise Unclassified Properties

Density, g/cm3 8.1
8.7
Embodied Carbon, kg CO2/kg material 2.7
35
Embodied Energy, MJ/kg 46
550

Common Calculations

Stiffness to Weight: Axial, points 7.3
5.8
Stiffness to Weight: Bending, points 20
17
Strength to Weight: Axial, points 17
5.4
Strength to Weight: Bending, points 17
7.8
Thermal Shock Resistance, points 16
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Copper (Cu), % 63 to 69.2
31 to 33
Iron (Fe), % 0 to 0.4
0
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0.8 to 1.2
0
Silver (Ag), % 0
34 to 36
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 30 to 36
31 to 35
Residuals, % 0
0 to 0.15