C87900 Brass vs. AWS E308L

C87900 brass belongs to the copper alloys classification, while AWS E308L belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is AWS E308L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 25
40
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 41
78
Tensile Strength: Ultimate (UTS), MPa 480
580

Thermal Properties

Latent Heat of Fusion, J/g 190
290
Melting Completion (Liquidus), °C 930
1420
Melting Onset (Solidus), °C 900
1380
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 120
16
Thermal Expansion, µm/m-K 20
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 17
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 24
16
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 2.7
3.2
Embodied Energy, MJ/kg 46
46
Embodied Water, L/kg 320
150

Common Calculations

Stiffness to Weight: Axial, points 7.3
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 37
4.1
Thermal Shock Resistance, points 16
15

Alloy Composition

Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
18 to 21
Copper (Cu), % 63 to 69.2
0 to 0.75
Iron (Fe), % 0 to 0.4
62.9 to 72.5
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0 to 0.5
9.0 to 11
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0.8 to 1.2
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 30 to 36
0