C87900 Brass vs. EN 1.0553 Steel

C87900 brass belongs to the copper alloys classification, while EN 1.0553 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is EN 1.0553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 25
20
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 41
73
Tensile Strength: Ultimate (UTS), MPa 480
530
Tensile Strength: Yield (Proof), MPa 240
330

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 130
400
Melting Completion (Liquidus), °C 930
1460
Melting Onset (Solidus), °C 900
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 120
51
Thermal Expansion, µm/m-K 20
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 17
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 24
1.9
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 46
19
Embodied Water, L/kg 320
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
93
Resilience: Unit (Modulus of Resilience), kJ/m3 270
290
Stiffness to Weight: Axial, points 7.3
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 37
14
Thermal Shock Resistance, points 16
17

Alloy Composition

Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.24
Copper (Cu), % 63 to 69.2
0 to 0.6
Iron (Fe), % 0 to 0.4
96.8 to 100
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0 to 1.7
Nickel (Ni), % 0 to 0.5
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0.8 to 1.2
0 to 0.6
Sulfur (S), % 0 to 0.050
0 to 0.040
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 30 to 36
0