C87900 Brass vs. EN 1.4669 Stainless Steel

C87900 brass belongs to the copper alloys classification, while EN 1.4669 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is EN 1.4669 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 25
28
Poisson's Ratio 0.31
0.27
Shear Modulus, GPa 41
78
Tensile Strength: Ultimate (UTS), MPa 480
780
Tensile Strength: Yield (Proof), MPa 240
450

Thermal Properties

Latent Heat of Fusion, J/g 190
290
Maximum Temperature: Mechanical, °C 130
1030
Melting Completion (Liquidus), °C 930
1420
Melting Onset (Solidus), °C 900
1370
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 120
15
Thermal Expansion, µm/m-K 20
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 17
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 24
13
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.6
Embodied Energy, MJ/kg 46
38
Embodied Water, L/kg 320
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
190
Resilience: Unit (Modulus of Resilience), kJ/m3 270
510
Stiffness to Weight: Axial, points 7.3
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 17
28
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 37
4.0
Thermal Shock Resistance, points 16
21

Alloy Composition

Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.045
Chromium (Cr), % 0
21.5 to 24
Copper (Cu), % 63 to 69.2
1.6 to 3.0
Iron (Fe), % 0 to 0.4
65.2 to 74.8
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
1.0 to 3.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.5
1.0 to 3.0
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.010
0 to 0.040
Silicon (Si), % 0.8 to 1.2
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030
Tin (Sn), % 0 to 0.25
0
Zinc (Zn), % 30 to 36
0