C87900 Brass vs. EN AC-44200 Aluminum

C87900 brass belongs to the copper alloys classification, while EN AC-44200 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C87900 brass and the bottom bar is EN AC-44200 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
72
Elongation at Break, % 25
6.2
Poisson's Ratio 0.31
0.33
Shear Modulus, GPa 41
27
Tensile Strength: Ultimate (UTS), MPa 480
180
Tensile Strength: Yield (Proof), MPa 240
86

Thermal Properties

Latent Heat of Fusion, J/g 190
570
Maximum Temperature: Mechanical, °C 130
170
Melting Completion (Liquidus), °C 930
590
Melting Onset (Solidus), °C 900
580
Specific Heat Capacity, J/kg-K 390
910
Thermal Conductivity, W/m-K 120
130
Thermal Expansion, µm/m-K 20
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
35
Electrical Conductivity: Equal Weight (Specific), % IACS 17
130

Otherwise Unclassified Properties

Base Metal Price, % relative 24
9.5
Density, g/cm3 8.1
2.5
Embodied Carbon, kg CO2/kg material 2.7
7.7
Embodied Energy, MJ/kg 46
140
Embodied Water, L/kg 320
1050

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
9.1
Resilience: Unit (Modulus of Resilience), kJ/m3 270
51
Stiffness to Weight: Axial, points 7.3
16
Stiffness to Weight: Bending, points 20
55
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
28
Thermal Diffusivity, mm2/s 37
59
Thermal Shock Resistance, points 16
8.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.15
85.2 to 89.5
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Copper (Cu), % 63 to 69.2
0 to 0.050
Iron (Fe), % 0 to 0.4
0 to 0.55
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0 to 0.35
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0.8 to 1.2
10.5 to 13.5
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0 to 0.25
0
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 30 to 36
0 to 0.1
Residuals, % 0
0 to 0.15