C87900 Brass vs. Grade FDCrV Steel

C87900 brass belongs to the copper alloys classification, while grade FDCrV steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is grade FDCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 41
80
Tensile Strength: Ultimate (UTS), MPa 480
1800

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 130
410
Melting Completion (Liquidus), °C 930
1450
Melting Onset (Solidus), °C 900
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 120
48
Thermal Expansion, µm/m-K 20
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 17
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 24
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.9
Embodied Energy, MJ/kg 46
26
Embodied Water, L/kg 320
49

Common Calculations

Stiffness to Weight: Axial, points 7.3
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 17
64
Strength to Weight: Bending, points 17
42
Thermal Diffusivity, mm2/s 37
13
Thermal Shock Resistance, points 16
53

Alloy Composition

Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Carbon (C), % 0
0.62 to 0.72
Chromium (Cr), % 0
0.4 to 0.6
Copper (Cu), % 63 to 69.2
0 to 0.12
Iron (Fe), % 0 to 0.4
97.8 to 98.8
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0.5 to 0.9
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0.8 to 1.2
0.15 to 0.3
Sulfur (S), % 0 to 0.050
0 to 0.025
Tin (Sn), % 0 to 0.25
0
Vanadium (V), % 0
0.15 to 0.25
Zinc (Zn), % 30 to 36
0