C87900 Brass vs. Grade Ti-Pd17 Titanium

C87900 brass belongs to the copper alloys classification, while grade Ti-Pd17 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is grade Ti-Pd17 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Elongation at Break, % 25
22
Poisson's Ratio 0.31
0.32
Shear Modulus, GPa 41
40
Tensile Strength: Ultimate (UTS), MPa 480
270
Tensile Strength: Yield (Proof), MPa 240
190

Thermal Properties

Latent Heat of Fusion, J/g 190
420
Maximum Temperature: Mechanical, °C 130
320
Melting Completion (Liquidus), °C 930
1660
Melting Onset (Solidus), °C 900
1610
Specific Heat Capacity, J/kg-K 390
540
Thermal Conductivity, W/m-K 120
21
Thermal Expansion, µm/m-K 20
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 17
7.1

Otherwise Unclassified Properties

Density, g/cm3 8.1
4.5
Embodied Carbon, kg CO2/kg material 2.7
36
Embodied Energy, MJ/kg 46
600
Embodied Water, L/kg 320
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
55
Resilience: Unit (Modulus of Resilience), kJ/m3 270
180
Stiffness to Weight: Axial, points 7.3
13
Stiffness to Weight: Bending, points 20
35
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 17
21
Thermal Diffusivity, mm2/s 37
8.8
Thermal Shock Resistance, points 16
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 63 to 69.2
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.4
0 to 0.2
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0
Nickel (Ni), % 0 to 0.5
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Palladium (Pd), % 0
0.040 to 0.080
Phosphorus (P), % 0 to 0.010
0
Silicon (Si), % 0.8 to 1.2
0
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0 to 0.25
0
Titanium (Ti), % 0
98.9 to 99.96
Zinc (Zn), % 30 to 36
0
Residuals, % 0
0 to 0.4