MakeItFrom.com
Menu (ESC)

C87900 Brass vs. SAE-AISI H26 Steel

C87900 brass belongs to the copper alloys classification, while SAE-AISI H26 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is C87900 brass and the bottom bar is SAE-AISI H26 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
210
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 41
80
Tensile Strength: Ultimate (UTS), MPa 480
720 to 2100

Thermal Properties

Latent Heat of Fusion, J/g 190
240
Melting Completion (Liquidus), °C 930
1810
Melting Onset (Solidus), °C 900
1760
Specific Heat Capacity, J/kg-K 390
410
Thermal Conductivity, W/m-K 120
22
Thermal Expansion, µm/m-K 20
12

Otherwise Unclassified Properties

Base Metal Price, % relative 24
45
Density, g/cm3 8.1
9.3
Embodied Carbon, kg CO2/kg material 2.7
8.1
Embodied Energy, MJ/kg 46
120
Embodied Water, L/kg 320
90

Common Calculations

Stiffness to Weight: Axial, points 7.3
12
Stiffness to Weight: Bending, points 20
21
Strength to Weight: Axial, points 17
22 to 63
Strength to Weight: Bending, points 17
19 to 39
Thermal Diffusivity, mm2/s 37
5.6
Thermal Shock Resistance, points 16
22 to 63

Alloy Composition

Aluminum (Al), % 0 to 0.15
0
Antimony (Sb), % 0 to 0.050
0
Arsenic (As), % 0 to 0.050
0
Carbon (C), % 0
0.45 to 0.55
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 63 to 69.2
0 to 0.25
Iron (Fe), % 0 to 0.4
73.3 to 77.5
Lead (Pb), % 0 to 0.25
0
Manganese (Mn), % 0 to 0.15
0.15 to 0.4
Nickel (Ni), % 0 to 0.5
0 to 0.3
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0.8 to 1.2
0.15 to 0.4
Sulfur (S), % 0 to 0.050
0 to 0.030
Tin (Sn), % 0 to 0.25
0
Tungsten (W), % 0
17.3 to 19
Vanadium (V), % 0
0.75 to 1.3
Zinc (Zn), % 30 to 36
0