C91100 Bronze vs. EN 2.4879 Cast Nickel
C91100 bronze belongs to the copper alloys classification, while EN 2.4879 cast nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C91100 bronze and the bottom bar is EN 2.4879 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 2.0 | |
| 3.4 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 39 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 1150 |
| Melting Completion (Liquidus), °C | 950 | |
| 1450 |
| Melting Onset (Solidus), °C | 820 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 460 |
| Thermal Conductivity, W/m-K | 63 | |
| 11 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 55 |
| Density, g/cm3 | 8.7 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 4.2 | |
| 8.3 |
| Embodied Energy, MJ/kg | 69 | |
| 120 |
| Embodied Water, L/kg | 440 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.4 | |
| 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 180 |
| Stiffness to Weight: Axial, points | 6.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 7.7 | |
| 16 |
| Strength to Weight: Bending, points | 9.9 | |
| 16 |
| Thermal Diffusivity, mm2/s | 20 | |
| 2.8 |
| Thermal Shock Resistance, points | 9.1 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.35 to 0.55 |
| Chromium (Cr), % | 0 | |
| 27 to 30 |
| Copper (Cu), % | 82 to 85 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 9.4 to 20.7 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.5 | |
| 47 to 50 |
| Phosphorus (P), % | 0 to 1.0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.0050 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.030 |
| Tin (Sn), % | 15 to 17 | |
| 0 |
| Tungsten (W), % | 0 | |
| 4.0 to 6.0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |